Shanghai Bress Aluminum Co.,Ltd --Optional specification,composition,mechanical properties,price and typical application of 5754

Aluminium 5754 has excellent corrosion resistance especially to seawater and industrially polluted atmospheres.
It has higher strength than 5251. This high strength makes Aluminium 5754 highly suited to flooring applications.
After rolling, Aluminium 5754 spontaneously softens until it reaches a stable condition.
Aluminium 5754 is typically used in: Treadplate/Shipbuilding/Vehicle bodies/Rivets/Fishing industry equipment/Food processing/Welded chemical and nuclear structures

Shanghai BRESS aluminum Co.,Ltd Optional specification of 5754
Optional specification	Temper	Thickness（mm）	Width*length （mm）	Adopted standard
Sheet	H12/H14/H16/H22/H24/H26 /H31/H36/F/O/H111/H111	0.2～～4.0	300~1600(width)*800~6000	GB/T 3380 EN 485 ASTM B209 JIS H4000
Plate	H112/F/O/H111/H22/H32 H12/H14/H111	4.0～～300.0	300~1600(width)*800~4000	GB/T 3380 EN 485 ASTM B209M JIS H4000
Coil	H12/H14/H16/H22/H24/H26 /H31/H36/F/O/H111/H111	0.15～～6.0	300~1600(width)*C	GB/T 3380 EN 485 ASTM B209 JIS H4000

5083 alloy (Chemical Composition Limits wt%)
Cu	Si	Fe	Mn	Mg	Zn	Cr	Ti	Pb.Bi	Al
0.1	0.4	0.4	0.5	2.6-3.6	0.20	0.3	0.15	/	Remainder

5052-O/H111(Typical Mechanical & Physical Properties)
Weldable	Machinability	Corrosion Resistance	Electrical Conductivity 20℃(68℉) (%IACS)	Digital Density (20℃)(g/cm3)
A	C	A	D	2.68
Tensile Strength (25°C MPa)	Yield Strength (25°C MPa)	Hardness(HB) 500kgf 10mm ball	Elongation 1.6mm(1/16in)thickness	Shearing Strength max. MPa
240	80	--	14	172

5083-H22(Typical Mechanical & Physical Properties)
Weldable	Machinability	Corrosion Resistance	Electrical Conductivity 20℃(68℉) (%IACS)	Digital Density (20℃)(g/cm3)
A	C	A	D	2.68
Tensile Strength (25°C MPa)	Yield Strength (25°C MPa)	Hardness(HB) 500kgf 10mm ball	Elongation 1.6mm(1/16in)thickness	Shearing Strength max. MPa
270	130	--	8	--

5754-H112(Typical Mechanical & Physical Properties)
Weldable	Machinability	Corrosion Resistance	Electrical Conductivity 20℃(68℉) (%IACS)	Digital Density (20℃)(g/cm3)
A	C	A	D	2.68
Tensile Strength (25°C MPa)	Yield Strength (25°C MPa)	Hardness(HB) 500kgf 10mm ball	Elongation 1.6mm(1/16in)thickness	Shearing Strength max. MPa
190	90	58	12	--

Explain:
Grade	Weldable	Machinability	Corrosion Resistance	Electrical Conductivity
A	Easy to welded	Excellent	Very good	55-63
B	Weldable in most of application cases	Very good	Good	50-55
C	Welding is restrained	Good	Average	40-50
D	Welding is not recommend	Not goood	Bad	30-40